Quick dry double matte PP synthetic film

Product Composition

Bidirectional stretched polypropylene film + double-sided quick-dry coating

Double-sided coating has a fine surface

Good stiffness, waterproof, moisture-proof, tear resistant, environmental protection

Provide a wide range of thickness to choose 120 um / 150 um/180 um / 200 um/250 um

Mainly used for offset printing, but also for letterpress and screen printing

Inspection item		Inspection method	Unit	120um double matte	150um double matte	180um double matte	200um double matte	250um double matte
Width deviation		GB/T6673	mm	±2	±2	±2	±2	±2
Visual		Appearance	-	No wrinkles, no obvious scars, no obvious spots
Thickness deviation	Limit thickness	GB/T6672	um	120±4	150±4	180±4	202±4	250±4
Thickness deviation	Average thickness	GB/T6672	um	120±3	150±3	180±3	202±4	250±3
Weight		Electronic balance	g	89±4	107±3	128±3	138±4	163±4
Coated weight		Electronic balance	g	7-9*2	7-9*2	7-9*2	7-9*2	7-9*2
Printed surface tension		GB/T14216	Dyn/cm	≥40	≥40	≥40	≥40	≥40
Fastness		3M810	Grade	≥4	≥4	≥4	≥4	≥4
Whiteness		GB7974	%	92±5	95±3	95±3	95±3	95±3
Gloss		ISO2813 60°	Gs	3-8	3-8	3-8	3-8	3-8
Opacity		ISO2471-77	%	92±3	95±3	96±3	96±3	96±3
Tensile strength	Longitudinal	GB/T1040	Mpa	≥40	≥40	≥50	≥50	≥50
Tensile strength	Transverse	GB/T1040	Mpa	≥100	≥100	≥120	≥120	≥120
Elongation at break	Longitudinal	GB/T1040	%	≤200	≤200	≤200	≤200	≤200
Elongation at break	Transverse	GB/T1040	%	≤100	≤100	≤100	≤100	≤100
Thermal shrinkage	Longitudinal	120℃/5min	%	≤5	≤3	≤3	≤3	≤3
Thermal shrinkage	Transverse	120℃/5min	%	≤3	≤2	≤2	≤2	≤2

Conventional thickness: 120 um um / 150/180 um um / 200/250 um

Applicable printing: Mainly used for offset printing, but also suitable for letterpress and screen printing

Recommended storage conditions: 25℃ humidity 65%

Widely used in business cards, tags, maps, covers, color single pages and other business printing