High density quick drying double matte pp synthetic film

Product Composition

High density composite film material + double side quick drying coating

Double-sided coating has a fine surface

Good stiffness, waterproof, moisture-proof, tear resistant, environmental protection

Provide a variety of thickness options 250um/300um/380um

Mainly used for offset printing, but also for letterpress and screen printing

Inspection item		Inspection method	Unit	250um double matte high density	300um double matte high density	380um double matte high density
Width deviation		GB/T6673	mm	±2	±2	±2
Visual		Appearance	-	No wrinkles, no obvious scars, no obvious spots
Thickness deviation	Limit thickness	GB/T6672	um	250±5	300±5	380±5
Thickness deviation	Average thickness	GB/T6672	um	250±4	300±4	380±4
Weight		Electronic balance	g	255±5	325±5	372±5
Coated weight		Electronic balance	g	(7-9)*2	(7-9)*2	(7-9)*2
Printed surface tension		GB/T14216	Dyn/cm	≥40	≥40	≥40
Fastness		3M810	Grade	≥4	≥4	≥4
Whiteness		GB7974	%	90±5	90±5	90±5
Gloss		ISO2813 60°	Gs	3-8	3-8	3-8
Opacity		ISO2471-77	%	94±3	95±3	96±3
Tensile strength	Longitudinal	GB/T1040	Mpa	≥40	≥200	≥200
Tensile strength	Transverse	GB/T1040	Mpa	≥70	≥160	≥160
Elongation at break	Longitudinal	GB/T1040	%	≤50	≤50	≤50
Elongation at break	Transverse	GB/T1040	%	≤50	≤50	≤50
Thermal shrinkage	Longitudinal	120℃/5min	%	≤5	≤5	≤5
Thermal shrinkage	Transverse	120℃/5min	%	≤3	≤3	≤3

Regular thickness: 250um/300um/380um

Applicable printing: Mainly used for offset printing, but also suitable for letterpress and screen printing

Recommended storage conditions: 25℃ humidity 65%

Widely used in business cards, tags, maps, covers, color single pages and other business printing